SS400 steel data sheet

JIS G3101 SS400 steel is one of the most commonly used hot rolled general structural steel. supplied as plates, sheets, flats, bars, sections etc. SS400 steel excels in machinability and weldability.

As per JIS G 3101 standard, Carbon (C), Silicon (Si) and Manganese (Mn) content of SS400 steel are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.

SS400 steel Chemical Composition(max %):

Grade	C. max	Si. max	Manganese	P. max	S. max
SS400	-	-	-	0.050	0.050

SS400 steel Mechanical Properties:

Grade	Yield Strength min. (Mpa)		Tensile Strength MPa	Elongation min. %			Impact Resistance min.[J]
Grade	Thickness ＜16 mm	Thickness ≥16mm	Tensile Strength MPa	Thickness ＜5mm	Thickness 5-16mm	Thickness ≥16mm	Impact Resistance min.[J]
SS400	245	235	400-510	21	17	21	-

SS400 steel Equivalent Grade:

EN10025:1990	FE360B
DIN17100	ST37-2
NFA 35-501	E24-2
EN10025-2	S235JR
ASTM	A283C, A36
UNI7070	FE360B
GB/T700	Q235B

Besides, SS400 steel melting point is 1430 Degree Celsius. SS400 steel Brinell Hardness is 160HB, SS400 steel density is 7850kg/m3, SS400 steel Young’s Modulus is 190-210Gpa.

For more detailed SS400 steel data sheet, welcome to communicate with BBN steel.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support