Q-BQB 310-2009 B320L Automobile structure steel plate

Q-BQB 310-2009 B320L Automobile structure steel plate Chemical Composition and Mechanical Property

Grade	C	Si	Mn	P	S	Alt
B320L	≤0.10	≤0.30	≤0.50	≤0.030	≤0.035	≥0.010

Grade	Down Yield Strength MPa	Tensile Strength MPa	Yield Ratio	Elongation % L₀= 5.65√S₀	180° Bending test Apex diameter
B320L	≥215	320~420	---	≥27	0a

Q-BQB 310-2009 B320L Automobile structure steel plate Application

Q-BQB 310-2009 B320L steel plate is mainly used for manufacture of automobile frames, beams, and other auto parts.

Q-BQB 310-2009 B320L Automobile structure steel plate Other Name

B320L Automobile structure steel plate, Q-BQB 310-2009 B320L steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support