Q-BQB 310-2009 SPFH590 Automobile structure steel plate

Q-BQB 310-2009 SPFH590 Automobile structure steel plate

Q-BQB 310-2009 SPFH590 Automobile structure steel plate Chemical Composition and Mechanical Property

Grade C Si Mn P S Alt
SPFH590 ≤0.18 ≤0.60 ≤2.00 ≤0.025 ≤0.025 ≥0.010
Grade Up yield strength
MPa
Tensile strength
MPa
Elongation %
L0=50mm, b=25mm
180° Bending test
Apex diameter
Nominal thickness mm Nominal thickness mm
1.6~
<2.0
2.0~
<2.5
2.5~
<3.25
3.25~
6.0
<3.25 ≥3.25
SPFH590 ≥420 ≥590 ≥19 ≥20 ≥21 ≥22 3a 3a

Q-BQB 310-2009 SPFH590 Automobile structure steel plate Application

Q-BQB 310-2009 SPFH590 steel plate is commonly used to produce automotive safety parts, car frame, wheels and other automotive structural parts with requirement for forming performance and high strength.

Q-BQB 310-2009 SPFH590 Automobile structure steel plate Other Name

Q-BQB 310-2009 SPFH590 steel plate, SPFH590 Automobile structure steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Contact Us

Henan BEBON Iron&Steel co.,ltd.

Send Order Request