Q-BQB 310-2009 SAPH310 Automobile structure steel plate

Q-BQB 310-2009 SAPH310 Automobile structure steel plate Chemical Composition and Mechanical Property

Grade	C	Si	Mn	P	S	Alt
SAPH310	≤0.10	≤0.30	≤0.50	≤0.035	≤0.035	≥0.010

Grade

Tensile strength
MPa

Up yield strength
MPa

Elongation %
L₀=50mm, b=25mm

180° Bending test
Apex diameter

Nominal thickness mm

＜6.0

6.0~
＜8.0

≥8.0

1.6~
＜2.0

2.0~
＜2.5

2.5~
＜3.15

3.15~
＜4.0

4.0~
＜6.3

≥6.3

＜2.0

≥2.0

SAPH310

≥310

≥185

≥175

≥33

≥34

≥36

≥38

≥40

≥41

Q-BQB 310-2009 SAPH310 Automobile structure steel plate Application

Q-BQB 310-2009 SAPH310 steel plate is mainly used in car frame, wheels and other automotive structural parts with requirement for forming performance.

Q-BQB 310-2009 SAPH310 Automobile structure steel plate Other Name

Q-BQB 310-2009 SAPH310 steel plate, SAPH310 Automobile structure steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support