Q-BQB 310-2009 B380CL Automobile structure steel plate

Q-BQB 310-2009 B380CL Automobile structure steel plate Chemical Composition and Mechanical Property

Grade	C	Si	Mn	P	S	Alt
B380CL	≤0.12	≤0.30	≤1.20	≤0.030	≤0.025	≥0.010

Grade	Down Yield Strength MPa	Tensile Strength MPa	Yield Ratio	Elongation % L₀= 5.65√S₀	180° Bending test Apex diameter
B380CL	thickness≤5.5mm, ≥260	380~480	---	≥32	0.5a
	thickness5.5~10.0mm, ≥235			≥28
	thickness10.0~14.0mm, ≥220			≥25

Q-BQB 310-2009 B380CL Automobile structure steel plate Application

B380CL steel plate is mainly used to produce car Roller-type wheel rim and spokes with good cold formability.

Q-BQB 310-2009 B380CL Automobile structure steel plate Other Name

Q-BQB 310-2009 B380CL steel plate, B380CL Automobile structure steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support