Q-BQB 310-2009 SPFH540 steel plate

Q-BQB 310-2009 SPFH540 steel plate Chemical Composition and Mechanical Property

Grade	C	Si	Mn	P	S	Alt
SPFH540	≤0.15	≤0.50	≤1.80	≤0.025	≤0.025	≥0.010

Grade	Up yield strength MPa	Tensile strength MPa	Elongation % L₀=50mm, b=25mm				180° Bending test Apex diameter
			Nominal thickness mm				Nominal thickness mm
			1.6~ ＜2.0	2.0~ ＜2.5	2.5~ ＜3.25	3.25~ 6.0	＜3.25	≥3.25
SPFH540	≥355	≥540	≥21	≥22	≥23	≥24	2a	3a

Q-BQB 310-2009 SPFH540 steel plate Application

Q-BQB 310-2009 SPFH540 steel plate is mainly used in car frame, wheels and other automotive structural parts with requirement for forming performance and high strength.

Q-BQB 310-2009 SPFH540 steel plate Other Name

Q-BQB 310-2009 SPFH540 steel plate, Automobile structure SPFH540 steel plate, SPFH540 Automobile structure steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support