GB 5310 10Cr9Mo1VNbN boiler steel pipe

GB 5310 10Cr9Mo1VNbN boiler steel pipe has not only high oxidation resistance and high temperature steam corrosion resistance, but also good impact toughness, high and stable durability and thermal strength. When the temperature is below 620 C, the applied stress of GB 5310 10Cr9Mo1VNbN boiler steel pipe is higher than that of austenitic stainless steel. The recommended design stress is about two times of T9 and 2.25Cr-1Mo steel at temperatures above 550 C.

Chemical Composition and Mechanical Property of GB 5310 10Cr9Mo1VNbN boiler steel pipe:

Grade

Chemical composition %

10Cr9Mo1VNbN

C

Si

Mn

Cr

Mo

V

Ni

Alt

Nb

N

P

S

0.08 ~0.12

0.20 ~0.50

0.30 ~0.60

8.00 ~9.50

0.85 ~1.05

0.18 ~0.25

≤0.40

≤0.020

0.06 ~0.10

0.030 ~0.070

≤0.020

≤0.010

Mechanical properties

Tensile strength

Yield strength

Elongation A

≥585 Mpa

≥415 Mpa

≥16 %

GB 5310 10Cr9Mo1VNbN boiler steel pipe can be used as high temperature superheater, reheater steel pipe, high temperature header and steam pipe for subcritical and supercritical boilers whose wall temperature is less than 625 C, as well as nuclear power heat exchanger and oil cracking unit furnace pipe.

GB 5310 10Cr9Mo1VNbN boiler steel pipe, 10Cr9Mo1VNbN boiler pipe, 10Cr9Mo1VNbN pipe

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.