Home > steel plate > Carbon and Low-alloy High-strength Steel > DIN 17100

DIN17100 St37-3 Carbon and Low-alloy High-strength Steel Plate

DIN17100 St37-3 Carbon and Low-alloy High-strength Steel Plate Chemical Composition and Mechanical Property

Grade	Chemical Composition(%)
C	Mn≥	Si	P	S
DIN17100 St37-3	0.17	1.60	0.55	0.040	0.040
Grade	Mechanical Property
Tensile Strength(MPa)	Yield Strength(MPa)	% Elongation in 2 in.(50mm) min	Impacting Test Temperature(°C)
DIN17100 St37-3	340-470	215-235	15-22	+20

DIN17100 St37-3 Carbon and Low-alloy High-strength Steel Plate Application

DIN17100 St37-3 Steel Plates are used in Construction of Bridges, Highway Construction and Other Engineering construction

DIN17100 St37-3 Carbon and Low-alloy High-strength Steel Plate Other Name

DIN17100 St37-3 Carbon Structural Steel Plate, DIN17100 St37-3 High Strength Structural Steel Plate, DIN17100 St37-3 Carbon Steel plate, DIN17100 St37-3 Structural Steel Plate.

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support