P265GH+410 Clad steel plate

P265GH+410 Clad steel plate Chemical Composition and Mechanical Property

Grade	Chemical Composition(%)
Grade	C max	Mn	Si max	P max	S max
EN10028-2 P265GH	0.2	0.8-1.4	0.40	0.025	0.015
Grade	Mechanical Property
Grade	Tensile Strength(MPa)	Yield Strength(MPa) min	% Elongation in 2 in.(50mm) min	Impacting Test Temperature(°C)
EN10028-2 P265GH	390-530	265	22	+20,0,-20

、

Grade

Cooper

410(S41000)

0.08-0.15

1.00

0.040

0.030

1.00

11.5-13.5

0.75

Grade

Yield strength

(N/mm2), min

Tensile strength (N/mm2), min

Elongationin 2 in. (50mm), %, min

Hardness, max
Brinell	Rockwell B

Cold bend

Austenitic (Chromium-Nickel) (Chromium-Manganese-Nickel)

410(S41000)

205

450

217

180

P265GH+410 Clad steel plate Application

P265GH+410 Clad steel plates are used in Construction of Bridges, Highway Construction and Other Engineering construction.

P265GH+410 Clad steel plate Other Name

P265GH+410 Clad steel plate, P265GH steel plate, 410 steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support