A516Gr70+410 Clad steel plate

A516Gr70+410 Clad steel plate Chemical Composition and Mechanical Property

Grade

Chemical Composition(%)

P max

S max

A516 Grade 70

(A516GR70)

0.27-0.31

0.79-1.3

0.13-0.45

0.035

Grade

Mechanical Property

Tensile Strength(MPa)

Yield Strength(MPa) min

% Elongation in 2 in.(50mm) min

Impacting Test Temperature(°C)

A516 Grade 70

(A516GR70)

485-620

260

-20,40,-60

Grade

Cooper

410(S41000)

0.08-0.15

1.00

0.040

0.030

1.00

11.5-13.5

0.75

Grade

Yield strength

(N/mm2), min

Tensile strength (N/mm2), min

Elongation in 2 in. (50mm), %, min

Hardness, max
Brinell	Rockwell B

Cold bend

Austenitic (Chromium-Nickel) (Chromium-Manganese-Nickel)

410(S41000)

205

450

217

180

A516Gr70+410 Clad steel plate Application

A516Gr70+410 Clad steel plates are used in Construction of Bridges, Highway Construction and Other Engineering construction.

A516Gr70+410 Clad steel plate Other Name

A516Gr70+410 Clad steel plate, A516Gr70 steel plate, 410 steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support