J 403-AISI 1060 steel plate

BEBON steel is J 403-AISI 1060 steel supplier,we have much experience in manufacture J 403-AISI 1060 steel, We could give the fastest delivery time on the base of our competitive price directly from our mill. if you need know steel grade feature,we can provide J 403-AISI 1060 chemical composition and J 403-AISI 1060 mechanical properties.

SAE J 403-AISI 1060 steel plate high carbon steel
1060 steel plate, SAE J 403-AISI 1060 steel plate, under SAE J 403-AISI standard, we can regard 1060 steel plate as high carbon steel.

SAE J 403-AISI 1060 carbon steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of carbon steels is about 7.85 g/cm3. SAE J 403-AISI 1060 typical tensile strength varies between 276 and 1882 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions ofSAE J 403-AISI 1060.

1060 steel plate is one mainly of high carbon steel,SAE J 403-AISI 1060 steel plate is one of the higher carbon content (0.60%) steels.It is more difficult to fabricate than the lower carbon grades.

1060 SAE J 403-AISI Number:1.0601	Comparision of steel grades
	JIS G 4051	S 58 C
	EN10083	C 60
	NFA 33-101	-
	UNI 7846	-
	BS 970	070 M 60
	UNE 36011	-
	SAE J 403-AISI	1060

Chemical Composition of C60 steel

Grade	C(%)min-max	Si(%)min-max	Mn(%)min-max	P(%)max	S(%)max	Cr(%)min-max
1060	0.57-0.65	0.15-0.35	0.60-0.90	0.025	0.025	0.20-0.40

Mechanical Properties of C60 steel

Grade	Condition	Yield Strength R°(Mpa)	Tensile Strength Rm (Mpa)	Elon- gation A5(%)	Hardness HRC	Quenching Temperature (℃)	Benda- bility	Nominal Thickness,t 1.95mm≤t≤10.0mm
								Rolled	Annealed
1060	Rolled Annealed Water-quenched Oil quenched	540 370	875 580 2670 2430	17 29	63 60	800 840	Min.reco-mmended Bending radius (≤90°)	3.0 ×t	1.0×t

If you need to buy J 403-AISI 1060 steel, we will strictly according to the customer put forward the specifications of the J 403-AISI 1060, chemical composition, performance requirements such as supply goods,if you anything pls contact us.