BV FH32 steel plate,BV Grade FH32 shipbuilding steel price,BV Grade FH32 steel supplier and manufacturer.
BV FH32 shipbuilding Steel Description:
All BV steels are standard carbon steels. As with other grades of steel, they have a specific gravity of 7.8.Higher-strength BV shipbuilding steel comes in six grades of two strengths, The BV FH 32 grade steel plates have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa).
BV FH32 Shipbuilding Steel Application:
BV FH32 Shipbuilding steel plates are suitable for container and bulk cargo vessels as well as cruise ships, ferries and yachts.
BV FH32 Steel Grade Specification:
Thickness: 4mm to 260mm,
Width: 1200mm to 4000mm
Length: 3000mm to 18000mm.
BV FH32 Ship Steel Delivery Conditions:
BV FH32 Delivery Condition: AR(As hot rolled only), TMCP, Q+T(Quenching+Tempering), N(Normalizing),CR( Control rolled only)
BVFH32 Steel Plate Additional Service:
Hot rolled(HR), control rolled(CR) Thermo Mechanical Control Process(TMCP), Normalized , Q&T, impact test, Z15,Z25,Z35.
BV FH32 Shipbuilding Steel Chemical Composition:
|
Grade |
C % |
Si % |
Mn % |
P % |
S % |
V % |
AL % |
Cr % |
|
BV Grade FH32 |
0.160 |
0.1-0.5 |
0.90-1.6 |
0.025 |
0.025 |
0.05-0.10 |
0.015 |
0.200 |
|
Cu % |
Mo % |
Nb % |
Ni % |
Ti % |
N % |
|
|
|
|
0.350 |
0.080 |
0.02-0.05 |
0.800 |
0.020 |
0.009 |
|
|
BV FH32 Grade Ship Steel Mechanical Properties:
| Grade |
Thickness(mm) |
MinYield(Mpa) |
Tensile(Mpa) |
Elongation (%) |
Min Impact Energy |
|
|
BV Grade FH32 |
8mm-50mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
34J |
|
51mm-70mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
41J |
|
|
71mm-100mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
50J |
|
|
The min impact energy is longitudinal energy |
||||||
BEBON BV FH32 shipbuilding steel plates and sheets have been exported to worldwide shipyard and ship building company,we have mill BV Grade FH32 for shipbuilding.If you have any needs in BV Grade FH32 steel plate price and suppliers, please feel free to contact us.