J 403-AISI 1055 steel plate

BEBON steel is J 403-AISI 1055 steel supplier,we have much experience in manufacture J 403-AISI 1055 steel, We could give the fastest delivery time on the base of our competitive price directly from our mill. if you need know steel grade feature,we can provide J 403-AISI 1055 chemical composition and J 403-AISI 1055 mechanical properties.

SAE J 403-AISI 1055 steel plate high carbon steel
1055 steel plate, SAE J 403-AISI 1055 steel plate, under SAE J 403-AISI standard, we can regard 1055 steel plate as high carbon steel.

SAE J 403-AISI 1055 carbon steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of carbon steels is about 7.85 g/cm3. SAE J 403-AISI 1055 typical tensile strength varies between 276 and 1882 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions of SAE J 403-AISI 1055.

1055 steel plate is one mainly of high carbon steel,UNE36011 1055 steel plate Comparied of steel grades JUS Č.1630,DIN C55, BS 070M55,GOST55 and AISI 1055 steel.

1055 SAE J 403-AISI Number:1.0535	Comparision of steel grades
	JIS G 4051	S 55 C
	DIN 17200	C 55
	NFA 33-101	AF70-C 55
	UNI 7846	C 55
	BS 970	070 M 55
	EN 10083-2	C 55
	SAE J 403-AISI	1055

Chemical Composition of C55K steel

Grade	C(%)min-max	Si(%)min-max	Mn(%)min-max	P(%)max	S(%)max	Cr(%)min-max
1055	0.52-0.60	0.15-0.35	0.60-0.90	0.025	0.025	0.20-0.40

Mechanical Properties of C55K steel

Grade	Condition	Yield Strength R°(Mpa)	Tensile Strength Rm (Mpa)	Elon- gation A5(%)	Hardness HRC	Quenching Temperature (℃)	Benda- bility	Nominal Thickness,t 1.95mm≤t≤10.0mm
								Rolled	Annealed
1055	Rolled Annealed Water-quenched Oil quenched	500 350	825 550 2510 2120	18 30	61 57	805 845	Min.reco-mmended Bending radius (≤90°)	3.0 ×t	1.0×t

If you need to buy J 403-AISI 1055 steel, we will strictly according to the customer put forward the specifications of the J 403-AISI 1055, chemical composition, performance requirements such as supply goods,if you anything pls contact us.