| C40E EN 10083-2:2002, Number: 1.1186
|
Comparison of steel grades | |
| JUS | Č.14342 | |
| DIN | Ck40, C40 | |
| BS | (080M40), CS40 | |
| GOST | 40 | |
| AISI | SAE 1040 | |
| UNI | - | |
| NF | (XC42H1), XC38 | |
Under EN 10083-2:2002 standard C40E Alloy steel properties and heat treatment forgings, Including C40E Alloy steel application and specifications, We have all specifications，Including C40E bars, rod, Plate, bar, square steel, rectangular steel,forgings, BEBON CHINA can own production and sales.
C40E Alloy steel Chemical analysis -% by mass
| Chemical elements | C | Si max. |
Mn | P max. | S1 max. |
Cr max. |
Mo max. |
Ni max. |
Cr+Mo+Ni max. |
| %,by mass |
0,37-0,44
|
0,40 | 0,50-0,80 | 0.025 | 0,035 | 0,40 | 0,10 | 0,40 | 0,63 |
| Permissible deviation | ± 0.02 | +0,03 | ± 0,04 | + 0.005 | + 0.005 | +0,05 | +0,03 | +0,05 | - |
| Distance in mm from quenched end Hardness in HRC (mm) | ||||||||||||||||||
| Symbol | mm→ | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 13 | 15 | 20 | 25 | 30 | |
| +H | max. | 60 | 60 | 59 | 57 | 53 | 47 | 39 | 34 | 31 | 30 | 29 | 28 | 27 | 26 | 25 | 24 | |
| min. | 51 | 46 | 35 | 27 | 25 | 24 | 23 | 22 | 21 | 20 | - | - | - | - | - | |||
Tentative values for the ’’C’’ scale Rockwell hardness for special steel grades with restricted hardenability scatter bands (+HH and +Hl grades)
| Symbol | Distance in mm from the quenched end HRC hardness | ||
| 1 | 4 | 5 | |
| +HH4 +HH14 +HL4 +HL14 | - | 38 to 57 | - |
| 54 to 60 | 38to 57 | - | |
| - | 27 to 46 | - | |
| 51 to 57 | 27 to 46 | - | |
Maximum hardness for products to be supplied in the ’’treated to improve shearability (+S)’’ or ’’soft annealed (+A)’’ condition
| +S (HB max.) | +A (HB max.) |
| - | - |
Mechanical properties in the quenched and tempered condition (+QT)
|
|
Mechanical properties for the ruling sections (see prEN10083-1:2002, Annex A) with a diameter (d) or for flat products trickness (t) of | ||||
| d ≤ 16mm t ≤ 8mm | 16mm < d ≤ 40mm 8mm < t ≤ 20mm | 40mm < d ≤ 100mm 20mm < t ≤ 60mm | |||
| Re min (MPa) | 460 | 400 | 350 | ||
| Rm (MPa) | 650-800 | 630-780 | 600-750 | ||
| A min. (%) | 16 | 18 | 19 | ||
| Z min. (%) | 35 | 40 | 45 | ||
| KV min. (J) |
30
|
30
|
30
|
||
Mechanical properties in the normalized condition – (+N)
|
|
Mechanical properties for products with a diameter (d) or, for flat products trickness (t) of | ||||
| d ≤ 16mm t ≤ 16mm | 16mm < d ≤ 100mm 16mm < t ≤ 100mm | 100mm < d ≤ 250mm 100mm < t ≤ 250mm | |||
| Re min. (MPa) | 320 | 290 | 260 | ||
| Rm min. (MPa) | 580 | 550 | 530 | ||
| A min. (%) |
16
|
17
|
17
|
||
Heat treatment conditions
| Quenching, 0C | Quenching agent | Tempering temperature, 0C | Hardening temperature in the end quench test, 0C | Normalizing, 0C |
| 830-870 | Water or oil | 550-660 | 8700±5 | 850 to 910 |
Source: