SEW092 QStE500N Automobile structure steel plate
SEW092 QStE500N Automobile structure steel plate Chemical Composition and Mechanical Property
| Grade | C % | Si % | Mn % max. | P % | S % | Al % min. | Nb % max | Ti % max |
| QStE500N | 0.22 | 0.50 | 1.70 | 0.03 | 0.03 | 0.015 | 0.09 | 0.22 |
| Grade | Yield Strength N/mm² mind. |
Tensile Strength N/mm² |
Elongation % | Technology bending test Mandrel diameter Da = Sample thickness bending angle180° |
|||
| Thickness＜3mm | ≥3mm≤6mm | ≥3mm | |||||
| L0= 80mm | L0= 50mm | L0= 50mm | L0= 5d0 | ||||
| QStE500N | 500 | 580bis730 | 14 | 15 | 18 | 19 | D=1a |
SEW092 QStE500N Automobile structure steel plate Application
QStE500N steel plate is mainly used for manufacture of Automobile structure parts.
SEW092 QStE500N Automobile structure steel plate Other Name
QStE500N Automobile structure steel plate, SEW092 QStE500N steel plate
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
Other Terms
Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Sales Department Team
Send Order Request Online Chat