Q/BQB 310-2009 SPFH590 Hot Rolled Steel Coil
Q/BQB 310-2009 SPFH590 Hot Rolled Steel Coil Chemical Composition and Mechanical Property
|
C max |
Si max. |
Mn max. |
P max. |
S max. |
Alt min. |
|
0.18 |
0.60 |
2.00 |
0.025 |
0.025 |
0.010 |
| Yield Strength (MPa) min. |
Tensile Strength (MPa) min. |
Elongation % min. |
||||
|
Thickness(mm) |
||||||
| 420 | 590 |
1.6≤t<2.0 |
2.0≤t<2.5 |
2.5≤t<t3.25 |
3.25≤t≤6.0 | |
|
19 |
20 |
21 | 22 | |||
Q/BQB 310-2009 SPFH590 Hot Rolled Steel Coil Application
Q/BQB 310-2009 SPFH590 hot rolled steel coil is mainly used for Automobile frames, beams, roll-type wheels, automotive transmission pipe, automobile axle housing and so on.
Q/BQB 310-2009 SPFH590 Hot Rolled Steel Coil Other Name
Q/BQB 310-2009 SPFH590 hot rolled steel coil, Q/BQB 310-2009 SPFH590 hot rolled steel coil price, Q/BQB 310-2009 SPFH590 hot rolled steel coil chemical composition
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
Other Terms
Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Sales Department Team
Send Order Request Online Chat