Q/BQB 310-2009 or JIS G3113-2006 SAPH370 Hot Rolled Steel Coil
Q/BQB 310-2009 or JIS G3113-2006 SAPH370 Hot Rolled Steel Coil Chemical Composition and Mechanical Property
|
C max |
Si max. |
Mn max. |
P max. |
S max. |
Alt min. |
|
0.21 |
0.30 |
0.75 |
0.035 |
0.035 |
0.010 |
|
Yield Strength (MPa) min. |
Tensile Strength (MPa) min. |
Elongation % min. |
||||||||
|
Thickness(mm) |
Thickness(mm) |
|||||||||
|
t<6.0 |
6≤t<8.0 |
8.0≤t≤25.4 |
370 |
1.6≤t<2.0 |
2.0≤t<2.5 |
2.5≤t<t3.15 |
3.15≤t<4.0 | 4.0≤t<6.3 |
6.3≤t≤25.4 |
|
|
225 |
225 |
215 |
32 |
33 |
35 |
36 | 37 |
38 |
||
Q/BQB 310-2009 or JIS G3113-2006 SAPH370 Hot Rolled Steel Coil Application
Q/BQB 310-2009 or JIS G3113-2006 SAPH370 hot rolled steel coil is mainly for Automobile frames, beams, roll-type wheels, automotive transmission pipe, automobile axle housing and so on.
Q/BQB 310-2009 or JIS G3113-2006 SAPH370 Hot Rolled Steel Coil Other Name
JIS G3113-2006 SAPH370 hot rolled steel coil, Q/BQB 310-2009 SAPH370 hot rolled steel coil
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
Other Terms
Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Sales Department Team
Send Order Request Online Chat