DIN 17102 StE255 Hot Rolled Steel Coil

DIN 17102 StE255 Hot Rolled Steel Coil Chemical Composition and Mechanical Property

C max	Si max.	Mn	P max	S max	N max.	All tot 1)	Cr max	Cu max	Mo max	Ni max	Nb max	Ti max	V max	Nb+Ti+V max
0.18	0.40	0.50-1.30	0.035	0.035	0.020	0.020	0.30	0.20	0.08	0.30	0.03	-	-	0.05

1) If nitrogen is additionally controlled by niobium, titanium or vanadim, the specification minimum aluminium content is dropped.

Yield Strength (MPa) min. (t≤16mm)	Yield Strength (MPa) min.(16mm<t≤25.4mm)	Tensile Strength (MPa)	Elongation % min.
255	245	360-480	25

DIN 17102 StE255 Hot Rolled Steel Coil Application

DIN 17102 StE255 hot rolled steel coil can be used for Automobile Frame, Construction of Bridges, Highway Construction and Other Engineering construction.

DIN 17102 StE255 Hot Rolled Steel Coil Other Name

DIN 17102 StE255 hot rolled steel, DIN 17102 StE255 hot rolled steel coil

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Sales Department Team

Send Order Request Online Chat