DIN 17102 WStE500 Carbon and Low-alloy High-strength Steel Coil

DIN 17102 WStE500 Carbon and Low-alloy High-strength Steel Coil Chemical Composition and Mechanical Property

C max	Si	Mn	P max	S max	N max.	All tot 1)	Cr max	Cu max	Mo max	Ni max	Nb max	Ti max	V max	Nb+Ti+V max
0.21	0.10-0.60	1.00-1.70	0.035	0.030	0.020	0.020	0.30	0.20	0.10	1.00	0.05	-	0.22	0.22

1) If nitrogen is additionally controlled by niobium, titanium or vanadim, the specification minimum aluminium content is dropped.

Yield Strength (MPa) min. (t≤16mm)	Yield Strength (MPa) min.(16mm<t≤25.4mm)	Tensile Strength (MPa)	Elongation % min.
500	480	610-780	18

DIN 17102 WStE500 Carbon and Low-alloy High-strength Steel Coil Application

DIN 17102 WStE500 carbon steel coil is used in the Construction of Bridges, Highway Construction and Other Engineering construction.

DIN 17102 WStE500 Carbon and Low-alloy High-strength Steel Coil Other Name

DIN 17102 WStE500 structural steel, WStE500 carbon steel coil, WStE500 structural steel coil

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Sales Department Team

Send Order Request Online Chat