| S235J2G3 Fe360D1 EN 10025-2:2002, Number: 1.0116 | Comparison of steel grades | |
| JUS | Č.0362, Č.0363 | |
| DIN | St.37-3 | |
| BS | 4360 | |
| GOST | - | |
| AISI | (A283, A366) | |
| UNI | - | |
| NF | - | |
S235J2G3 steel plate Chemical analysis -% by mass
| Chemical elements | C ** max. | Si max. |
Mn max. | P max. | S max. |
Cr max. |
Mo max. |
Ni max. |
Cr+Mo+Ni max. |
Al min. |
| %, by mass | 0,17 | 0,55 | 1,40 | 0,035 | 0,035 | 0,30 | 0,08 | 0,30 | 0,48 | 0,020 |
| Permissible deviation | + 0,02 | + 0,03 | + 0,04 | + 0,005 | + 0,005 | + 0,05 | + 0,03 | + 0,05 | - 0,005 |
At the option of the manufacturer the elements aluminium, titanium, vanadium and niobium may be added singly or in combination for grain size control purposes. Elements not quoted in table shall not be added to the steel without the agreement of the purchaser, except for the purpose of finishing the heat. For forging with an equivalent diameter or thickness >100mm the carbon content shall be agreed between purchaser and supplier. Mechanical properties in the normalized and normalized and tempered conditions
| Thickness of ruling section tR | |||||
| Diameter in mm | tR ≤ 100mm | 100< tR ≤250mm | 250< tR ≤500mm | 500< tR ≤1000mm | |
| Re min (N/mm2) | 215 | 175 | 165 | - | |
| Rm min (N/mm2) | 340 | 340 | 340 | - | |
| A % min. | l-longitudinal | 24 | 23 | 23 | - |
| tr -transverse | - | 17 | 17 | - | |
| KV min * (J) | l-longitudinal | 35 | 30 | 27 | - |
| tr -transverse | - | 20 | 15 | - | |
1N/mm2=1MPa
* Impact testing shall be carried out at -200C. Heat treatment conditions
| Normalizing temperature, 0C |
| 890 to 950 |
Source:
Tags: S235J2G3 Fe360D1